Welding Through Rusty Metal Tips And Tricks | Weld Through Rust | Flux Core Welding For Beginners |

In today's episode of how to learn flux core welding for beginners, I cut up some pieces of scrap steel to show you guys the drawbacks of welding on rusty dirty metal. The process is not too different from welding on your own with clean metal, but it does take some precautions. Follow along this short video so you can learn what to expect when welding rusty and dirty metals.

#Fluxcorewelding #Rust #Welding


The video had to be shot completely 3 times over because I could not get all the info to fit in a tiny video. Flux core welding is relatively cheap and easy to do, plus you don't need anything fancy to do what you need to get done. Today I'll be showing you guys how to set up your welder for welding with flux core. Although getting the hang of your hand control is the biggest issue with bad welds, the rest will fall on setting up the machine settings for flux core as well. Please remember that these machines have to be set up with electrode positive.

#fluxcorewelding #howtoweld #gasslesswelding

his is another long one fellas. Way too many of you guys are asking about this so instead of replying to each of you one at a time I'm just going to link this video for you and hopefully it helps out your flux core welding. I might become a flux core welding channel pretty soon lmao. Basically in the video I show you guys how to take a regular gasless welder and use it to weld upwards or vertical. Once you get the hang of it, its not that hard so as long as you keep trying, it should all work out!

How To Weld Flux Core Vertical Or Upwards For Beginners | Gasless Welding Tips and Tricks |

#fluxcore #Welding #Weldingtricks

Several people thought the flux core process was weak and dirty so this video is to basically test to see how well the welding process actually works. Settings are the same as last time and the welder is a vulcan omnipro 220 welder from harbor freight tools. Let me know if there are any other videos you guys want to see about welding and welding accessories.

How Strong Is Flux Core Welding? | Gasless Flux Core Welding For Beginners Tips And Tricks |

Learn how to take your basic welding skills to the next level with 5 easy things your can do to have better performing welds in less than 10 mins. I go through 5 easy ways to weld flux core wire and make it look like gas mig welds. You can take these tips and tricks to better your hand control and finally get the welding results you are looking for. Flux core welding for beginners is the best way to learn how to make clean and concise welds with just a little bit of effort. It only takes a little bit of practice and you will be welding like a pro in no time at all. Tools used in the video are the vulcan 220 welder from harbor freight. Slag hammer from harbor freight. Tig welding gloves from harbor freight and Lincoln flux core welding wire size .030.

Learn Perfect Flux Core Welds In 10 Mins | Gasless Flux Core Welding For Beginners Tips And Tricks |

[NightWrencher]

Theres a whole flux core welding playlist here on the channel full of videos like this so check it out!

[NiklasLarssonSeglarfan]

Is it enough to just grind away the rust? Cause i did some stick-welding on really rusty old metal, the stuff that's sat outside for 20+ years. I did grind it clean before the welds, but i still couldnt get a proper nice puddle or bead, almost all came out horrible and inconsistent. I'm typically a pretty good stick-welder, but for that project i couldnt get anything done right.. Thinking maybe the metal underneath the rust is still so heavily affected that it doesnt matter if you grind it clean or not? I did work with very cheap welder and the cheapest electrodes money can buy, so it may also have affected.

[nat.]

Does the Rusty ground also cause non continuous arc issue ?

[infamousnova]

An I need those gloves, the ones I have are big and irritating.

[DirtyBikerbits]

Plasma cut areas aren't clean, they're contaminated with dross and oxides, they just happen to be less dirty than the rest of what's being welded